InIconel 713 lc isometric nickel-based precipitation hardening type iphosa ialloy yobushushu obuphezulu, yimodification alloy Inconel 713 c, ukusetyenziswa kwamaqondo obushushu angaphantsi kwe900 xa kuthelekiswa neInconel 713 c alloy, ukunciphisa umxholo wekhabhoni wokulungelelanisa umxholo wechromium kunye nemolybdenum alloy. inokumelana kakuhle nokugqabhuka kunye nokubanda kunye nokumelana nokudinwa okubandayo, kwaye iphucula kakhulu iplastiki yobushushu begumbi, ukusebenza kwempembelelo kunye nokusebenza kombutho okuzinzileyo Oku kusebenza kakuhle ekusetyenzisweni kwe-injini yokuphosa edibeneyo inokuphakama okukhulu.
Ukongeza, i-alloy ayikhathaleli ubungakanani becandelo kunye nesantya sokupholisa sokuphosa, ngoko ke ifanelekile ukuphosa ii-castings ezinkulu kunye necandelo elingaphezulu kwe-130mm.
Ingxubevange | % | Fe | Cr | Ni | Mo | Nb | Co | C | Mn | Si | S | Cu | Al | Ti | P | B | Zr |
713LC | Min. |
| 11.0 | ibhalansi | 3.8 | 1.5 | - | 0.03 | - | - | - | - | 5.5 | 0.4 | - | 0.005 | 0.05 |
Max. | 0.5 | 13.0 | 5.2 | 2.5 | 1.0 | 0.07 | 0.25 | 0.5 | 0.015 | 0.5 | 6.5 | 1.0 | 0.015 | 0.015 | 0.15 |
Ukuxinana | 8.01 g/cm³ |
Indawo yokunyibilika | 1288-1321 ℃ |
Ubume | Tensile strength Rm N/mm² | Unikeze Amandla Rp 0. 2N/mm² | Elongation Njenge % |
Unyango lwesisombululo | - | 760 | 9.5 |
Ukusebenza kwe-Inconel 713LC welding:
I-Electron beam welding, i-argon arc welding, i-isothermal solidification diffusion welding kunye ne-friction welding inokwenziwa.
I-alloy yayisetyenziswe kwi-aeroengine inkululeko ye-injini ye-injini ye-injini ye-injini ye-injini ye-injini ye-injini ye-injini ye-injini ye-injini ye-injini ye-injini ye-injini ye-injini ye-injini ye-injini ye-injini ye-injini ye-injini ye-disc, kunye nemveliso. ixesha elide lokusetyenziswa kombane odityanisiweyo wokwenziwa kombane weijini yomoya ngeinjini yegesi, njl